Silicone heat-resistant paint
Features:
Silicone high-temperature resistant paint is a coating made of silicone resin, special high-temperature resistant and anti-corrosion pigment fillers, additives, etc.
Excellent heat resistance, good adhesion, oil and solvent resistance. Drying at room temperature, fast drying speed.
Use:
The outer wall of the high-temperature reaction furnace, the transportation pipeline of the high-temperature medium, the chimney, the heating furnace, etc., require the coating of high-temperature and corrosion-resistant metal surfaces.
SILICONE HEAT-RESISTANT PAINT
PRODUCT PARAMETERS
| Coating appearance | The coating film is flattened | ||
| Color | Aluminum, silver, or a few other colors | ||
| Drying time | Surface dry ≤ 30min (23°C) Dry ≤ 24 h (23°C) | ||
| Ratio | 5:1(Weight Ratio) | ||
| Adhesion | Level ≤1 (Grid) | ||
| The recommended number of coatings |
2-3 channels, dry film thickness 70μm | ||
| Density | Approx. 1.2g/cm³ | ||
| Overcoat interval | |||
| Substrate temperature | 5℃ | 25℃ | 40℃ |
| Short time | 18h | 12h | 8h |
| Long time | No limit | ||
| Remark | When the post-coat is applied, the paint film should be dry, and the front paint film should not be polluted | ||
1. The surface must be clean, dry and free of any pollution
2. When the anti-corrosion level is high, the anti-rust grade of the coated surface reaches St3 or Sa2.5
PRODUCT DESCRIPTION
Organic high-temperature resistant paint is a coating made of silicone resin, special high-temperature resistant and anti-corrosion pigment fillers, additives, etc. Excellent heat resistance, good adhesion, oil and solvent resistance. Drying at room temperature, fast drying speed.
Construction conditions: The temperature of the substrate is at least higher than 3°C to prevent condensation, and the relative humidity is ≤ 80%.
Mixing: Stir component A well, then add component B (curing agent) to mix, and stir thoroughly.
Dilution: Components A and B are mixed evenly, an appropriate amount of supporting diluent can be added, stirred evenly, and adjusted to the construction viscosity.
The construction site should have a good ventilation environment to prevent the inhalation of solvent gases and paint mist. The product should be kept away from the heat source, and smoking is strictly prohibited on the construction site.
SCOPE OF APPLICATION
The outer wall of the high-temperature reaction furnace, the transportation pipeline of the high-temperature medium, the chimney, the heating furnace, etc., require the coating of high-temperature and corrosion-resistant metal surfaces.